Abstract and subjects
In situ neutron powder diffraction experiments are applied to physical, kinetic, and microstructural characterization of uranium mononitride as a promising light water reactor fuel material. The temperature-variable coefficient of thermal expansion and isotropic Debye Waller factors are obtained by sequential Rietveld refinement over 499–1873 K. Oxidation of a UN pellet (95.2% density) under flow of 11 mg/min D2O is observed to initiate above 623 K and the rate increases by a factor of approximately 10 from 673 to 773 K, with activation energy 50.6 ± 1.3 kJ/mol; uranium oxide is the only solid corrosion product.